In the process of understanding powder metallurgy technology, we were exposed to the metal powder injection molding process. I did not expect that it is completely different from ordinary molding technology. There must be no difficulty in mass-producing parts with complex geometries, high performance, and high precision. In order to promote breakthroughs in the industrialization of powder machining enterprises.

The starting point of powder metallurgical flow warm pressing technology
The starting point of powder metallurgical flow warm pressing technology

When powder metallurgy enterprises perform metal powder injection molding, in addition to preparing the corresponding powder required for processing, they also need to add more binders to the powder. Therefore, both powder and binder should meet the requirements, otherwise it will affect the forming of powder metallurgy products.

Among them, the powder needs to use ultra-fine near-spherical powder ≤ 10um, and from mixing to degreasing and sintering, the process is more complicated and the process requirements are strict, especially the longer degreasing and sintering time, which also causes the manufacturing cost of powder metallurgy enterprises to be partial The main reason for the high. The adhesive wolf must be sufficient, otherwise it is difficult to achieve the corresponding performance.

In this regard, a simplified method developed by the powder metallurgy enterprise is the flow warm pressing technology, which is based on the metal powder warm pressing and combines the advantages of the metal powder injection molding process; then by adding an appropriate amount of coarse powder and fine Powder, and increasing the content of thermoplastic lubricants, thereby greatly improving the flowability, filling properties and formability of the mixed powder.

Because the mixed powder becomes a viscous fluid with good fluidity during pressing, it not only has the advantages of a liquid, but also has a high viscosity and reduces friction. Only then can the pressing pressure be evenly distributed in the powder. Got a good pass. Because of this, the powder can flow to all corners without cracks during the pressing process, thereby greatly improving the density.

At present, powder metallurgy companies have promoted this technology for precision forming of workpieces with very complex shapes on traditional tablet presses, which not only overcomes the disadvantages of traditional cold pressing in forming complex geometries, but also avoids the high level of injection molding technology.

Link to this article: The starting point of powder metallurgical flow warm pressing technology

Reprint Statement: If there are no special instructions, all articles on this site are original. Please indicate the source for reprinting:,thanks!

cnc machining shopPTJ® provides a full range of Custom Precision cnc machining china services.ISO 9001:2015 &AS-9100 certified. 3, 4 and 5-axis rapid precision CNC machining services including milling, turning to customer specifications,Capable of metal & plastic machined parts with +/-0.005 mm tolerance.Secondary services include CNC and conventional grinding, drilling,die casting,sheet metal and stamping.Providing prototypes, full production runs, technical support and full inspection.Serves the automotiveaerospace, mold&fixture,led lighting,medical,bicycle, and consumer electronics industries. On-time delivery.Tell us a little about your project’s budget and expected delivery time. We will strategize with you to provide the most cost-effective services to help you reach your target,Welcome to Contact us ( ) directly for your new project.

Reply Within 24 Hours

Hotline:+86-769-88033280 E-mail:

Please place file(s) for transfer in the same folder and ZIP or RAR before attaching. Larger attachments can take a few minutes to transfer depending on your local internet speed :) For attachments over 20MB, click  WeTransfer and send to

Once all fields are filled in you will be able to send your message/file :)